Complete Refractory Solutions
Home
Products >> Orind Products China >> Monolithic
 
Monolithic Details
 

Our complete range of ultra low cement castable, low cement castable, conventional castable,  high alumina ramming mass, ladle back fill  & mortar for different application in Steel Ladle, Hot Metal Ladle, Hot Metal Mixer etc.
Brand Name Chemical Analysis Physical Analysis Sieve Analysis (%)
  Al2O3% (Min) SiO2%  (Max) Fe2O3% (Max) TiO2% (Max) Cr2O3% BD (g/cc) min. after drying at 110ºC/24hr CCS (MPa) min. after drying at 110ºC/24hr Max Grain Size (mm) +1 mm (+16#) +0.4 mm (+35#) - 0.1 mm     (-150#)
DENSE CASTABLES                      
ORIND SC-1450/1600/1650 65 20 3.0     2.1 45.0 5 40±4 - 35±4
ORIND SC-1600SF 65 20 3.0     2.25 55.0 5 40±4 - 35±4
ORIND SC-1750 80 6 2.5 3.0   2.60 50.0 5 35±4 - 35±4
ORIND SC-1850 85 4 2.0 3.0   2.85 50.0 5 45±4 - 35±4
ORIND SC-1900 88 3 1.8 2.5   2.85 55.0 5 45±4 - 35±4
SPECIAL DENSE CASTABLES                      
ORICAST 65 65 - -     2.5 60.0 5 45±4 - 35±3
ORIND SC-1950 90 2.5 1.5 2   2.9 60.0 5 45±4 - 35±3
ORIND SC-1950 C 90 2.5 1.5 2 1-2 2.9 60.0 5 45±4 - 35±3
ORICAST 95 92 - 1.5     3.08 60.0 5 40±4 - 35±3
ORICAST 97 97 - 0.5     3.0 40.0 5 40±4 - 35±3
LOW CEMENT CASTABLES         CaO%   (Max)            
ORIND LC 45 45 - 1.2   3.0 2.3 55 5 45±4 - 35±3
ORIND LC 60 60 - 1.2   3.0 2.6 60 5 45±4 - 35±3
ORIND LC 70 70 - 1.2   3.0 2.75 80 5 45±4 - 35±3
ORIND LC 80 80 - 1.5   3.0 2.85 80 5 45±4 - 35±3
ORIND LC 90 90 - 1.2   3.0 3 85 5 45±4 - 35±3
SPECIAL LOW CEMENT CASTABLES                      
ORIND LC 60A 56 - 1.5   3.0 2.5 65 5 45±4 - 35±3
ORIND LC 80 XC 80 - 1.5   3.0 2.95 90 20 53±4 - 35±3
LIPCAST 80 80 - 1.5   3.0 2.85 90 5 40±4 - 35±3
ORIND LC 95 93 - 1.0   3.0 3.0 40.0 5 45±4 - 35±3
SPINCAST 95 92 - 0.5   3.0 3 50 10 53±4 - 35±3
Brand Name Chemical Analysis Physical  Analysis Sieve Analysis (%)
  Al2O3  % (Min) SiO2  % (Max) Fe2O3  % (Max) Others  % BD (g/cc) min. after drying at 110ºC/24hr CCS (MPa) min. after drying at 110ºC/24hr Max Grain Size (mm) +1 mm (+16#) +0.4 mm (+35#) - 0.1 mm     (-150#)
ULTRA LOW CEMENT CASTABLES                    
ORIND ULC 45 45 - 2   2.4 45 5 40±5 - 45±3
TRUFCAST 65 65 - 1   2.85 70 5 40±5 - 45±3
ORIND ULC 80 80 MgO:    (5-10) 2 TiO2 <1.5  CaO < 2.0 2.85 65 5 35±5 - 35±4
ORIND ULC 90 85 MgO:    (5-10) 1 TiO2 <1.0  CaO < 2.0 3.0 45 5 30±5 - 35±4
HIGH ALUMINA RAMMING MASSES                    
ORIND ALCOR 70 70 - 2.5 - 2.65 20 5 40±5 - 45±3
ORIND ALCOR 80 75 15 5 TiO2 <5 2.65 30 5 40±5 - 45±3
ORIND ALCOR 90/90B 90 - 1.2 - 2.9 30 5 45±5 - 35±4
ORIND ALCOR 95H 95 - 0.5 - 2.9 40 3 35±5 - 30±4
MORTARS                    
AEROSET 50     (AL-50) 50 15 - -     0.5 NIL 1 Max 70 Min
AEROSET 60     (AL-60) 60 15 - -     0.5 NIL 1 Max 70 Min
AEROSET 70     (AL-70) 70 15 - -     0.5 NIL 1 Max 70 Min
AEROSET 80     (AL-80) 80 12 - -     0.5 NIL 1 Max 70 Min
KEMSET 70 70 - 1.5 -     0.5 NIL 1 Max 70 Min
KEMSET 90 K / M 90 4 - Cr2O3 <2     0.5 NIL 1 Max 90 Min
AIRSET 80M  (Ready to use) 80 15 - -     0.5 NIL 1 Max 70 Min
FILLING MASSES                    
BACKFILL 80A / ORIFILL 80A 80 6 3 TiO2 <4     3 30±5 - 25±5
 

Our full range of Magnesite base ramming mass, gunning mass, spraying mass & filling mass for various Ladle, BOF, EAF & Tundish application:
Brand name Chemical Analysis Physical Analysis Sieve Analysis (%)
  MgO% (Min) SiO2% (Max) OTHERS  % BD (g/cc) min. after drying at 110ºC/24hr CCS (MPa) min. after drying at 110ºC/24hr Max Grain Size(mm) +1 mm (+16#) +0.4 mm (+35#) - 0.1mm (-150#)
RAMMING MASSES                  
ORIND SUPERMAGRAM-1 90 2   2.6   4 45±5 - 26±4
ORIND SUPERMAGRAM (or SUPERMAGRAM-2) 90 2 Cr2O3 : (1-2) 2.5 AP <25%, CCS >25MPa 4 45±5 - 26±4
ORIND SUPERMAGRAM-3 90 2 P2O5 <3 2.5   4 45±5 - 26±4
CASTABLES FOR TAP HOLE 90 2       4 45±5 - 26±4
ORIND OXIMAGRAM 85 2 C >10 2.6 25 6 45±5 - 26±4
ORIND DRYHEARTH                         (DRY RAMMING MASS) 75   CaO >7 2.75   10 45±5 - 26±4
GUNNING MASSES                  
ORIND ARCGUN 85 7   2.5 30 4 45±5 - 25±5
ORIND SUPERARCGUN 85 7   2.5 30 4 45±5 - 25±5
ORIND ARCGUN 90C 88 5 Cr2O3 <2 2.75 35 4 45±5 - 30±5
ORIND ARCGUN 90P 80 5 P2O5 <3 2.75 35 4 45±5 - 30±5
ORIND ARCGUN 95C 90 3 Cr2O3 <2 2.8 40 4 45±5 - 30±5
ORIND OXIGUN 80 7 LOI <10 2.85 25 5 35±5 - 36±4
PATCHING MASSES                  
ORIND OXYPATCH (HOT PATCH) 60 7       5 50±5 - 25±5
ORIND ARCFET-1 75 2       10 45±5 - 20±5
ORIND ARCFET-2 80 3       10 45±5 - 20±5
FILLING MASSES                  
EBT FILLING MASS 45 -       8 90±5 - NIL
ORIND BACKFILL 70M 60-70 20 Al2O3 <10     3 30±5 - 25±5
ORIND ORIFILL 70M 70 20 Fe2O3 <5     3 30±5 - 25±5
TUNDISH COATING MASSES                  
ORIND TSPRAY 1 66 25   1.8   0.5 NIL 5 Max 45±5
ORIND TSPRAY 2 85 7   1.85   0.5 NIL 5 Max 45±5
ORIND TGUN 1 90 3   1.8   1 NIL 10±5 45±5
MORTAR                  
MAG MORTAR /  80% MgO MORTAR 80 10       0.5 NIL 1 Max 70 Min
PREMIX 95 -       - NIL 1 Max 90 Min
SLAG CONDITIONER 57 - LOI <25     - - - -
 